Structure and tribological behavior of Pb-Ti/MoS2 nanoscaled multilayer films deposited by magnetron sputtering method
Li, Hao; Xie, Mingling; Zhang, Guangan; Fan, Xiaoqiang; Li, Xia; Zhu, Minhao; Wang, Liping
2018
Source PublicationAPPLIED SURFACE SCIENCE
Volume435Pages:48-54
AbstractThe Pb-Ti/MoS2 nanoscaled multilayer films with different bilayer period were deposited by unbalanced magnetron sputtering system. The morphology, microstructure, mechanical and tribological properties of the films were investigated. It was found that the film changed from multilayer structure to composite structure as the bilayer period decreased from 25 nm to 6 nm, due to the diffusion effect. The multilayer film showed a pronounced (002) diffraction peak, the growth of the MoS2 platelets below the interface were affected by Pb and Ti, and the c-axis of MoS2 platelets were inclined to the substrate at an angle of -30 degrees to 30 degrees. The hardness of the film ranged from 5.9 to 7.2 GPa depending on the bilayer period. The tribological behavior of the films was performed under vacuum, and the friction coefficient were typically below 0.25. Furthermore, the nanoscale multilayer film with a bilayer period of 20 nm exhibits much better mechanical and tribological properties than pure MoS2. The result indicates that the nanoscale multilayer is a design methodology for developing high basal plane oriented and vacuum solid lubricating MoS2 based materials. (c) 2017 Published by Elsevier B.V.
KeywordZero-valent Iron Mos2 Thin-films Low-friction Composite Coatings Ultrahigh-vacuum Wear Orientation Growth Mechanisms Reactivity
Subject AreaChemistry ; Materials Science ; Physics
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/16740
Collection2018专题
Recommended Citation
GB/T 7714
Li, Hao,Xie, Mingling,Zhang, Guangan,et al. Structure and tribological behavior of Pb-Ti/MoS2 nanoscaled multilayer films deposited by magnetron sputtering method[J]. APPLIED SURFACE SCIENCE,2018,435:48-54.
APA Li, Hao.,Xie, Mingling.,Zhang, Guangan.,Fan, Xiaoqiang.,Li, Xia.,...&Wang, Liping.(2018).Structure and tribological behavior of Pb-Ti/MoS2 nanoscaled multilayer films deposited by magnetron sputtering method.APPLIED SURFACE SCIENCE,435,48-54.
MLA Li, Hao,et al."Structure and tribological behavior of Pb-Ti/MoS2 nanoscaled multilayer films deposited by magnetron sputtering method".APPLIED SURFACE SCIENCE 435(2018):48-54.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, Hao]'s Articles
[Xie, Mingling]'s Articles
[Zhang, Guangan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, Hao]'s Articles
[Xie, Mingling]'s Articles
[Zhang, Guangan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, Hao]'s Articles
[Xie, Mingling]'s Articles
[Zhang, Guangan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.