Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films
Li Lei; Guo Peng; Liu Lin-Lin; Sun Li-Li; Ke Pei-Ling; Wang Ai-Ying
2018
Source PublicationJOURNAL OF INORGANIC MATERIALS
Volume33Issue:3Pages:331-338
AbstractGraphite-like carbon films (GLC) with different metal buffer layers (Cr, Ti, W) were fabricated by direct current magnetron sputtering technique. The effect of metal buffer layer on structure and tribological properties in artificial seawater were carefully investigated. The results show that, in contrast to Ti/GLC and W/GLC film, Cr/GLC film has the highest sp(2) hybridization content, which increases from the top layer to Cr/C interface. The highest sp2 hybridization content promotes graphitization degree of the tribo-film which acts as lubrication phase in the sliding process. The results of potentiodynamic polarization tests show that, in all of three GLC films, Cr/GLC film shows superior corrosion resistance with the highest corrosion voltage (E-corr) of -0.16 V and the lowest corrosion current (i(corr)) of 4.42x10(-9) A/cm(2). As a result, Cr/GLC film presents the best tribological properties in artificial seawater in contrast to Ti/GLC and W/GLC films.
KeywordCarbon-films Coatings Environments Performance Deposition Adhesion Water Friction Behavior Ti6al4v
Subject AreaMaterials Science
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/16752
Collection2018专题
Recommended Citation
GB/T 7714
Li Lei,Guo Peng,Liu Lin-Lin,et al. Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films[J]. JOURNAL OF INORGANIC MATERIALS,2018,33(3):331-338.
APA Li Lei,Guo Peng,Liu Lin-Lin,Sun Li-Li,Ke Pei-Ling,&Wang Ai-Ying.(2018).Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films.JOURNAL OF INORGANIC MATERIALS,33(3),331-338.
MLA Li Lei,et al."Metal Buffer Layer on Structure, Mechanical and Tribological Property of GLC films".JOURNAL OF INORGANIC MATERIALS 33.3(2018):331-338.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li Lei]'s Articles
[Guo Peng]'s Articles
[Liu Lin-Lin]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li Lei]'s Articles
[Guo Peng]'s Articles
[Liu Lin-Lin]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li Lei]'s Articles
[Guo Peng]'s Articles
[Liu Lin-Lin]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.