A multiscale hydrothermal carbon layer modified carbon fiber for composite fabrication
Xi, Xianfeng; Chen, Yousi; Wang, Jie; Li, Yaoyao; Shao, Xiangdong; He, Liu; Huang, Qing; Pei, Xueliang
2018
发表期刊RSC ADVANCES
卷号8期号:41页码:23339-23347
摘要A novel multiscale hydrothermal carbon layer (MHTCL) for carbon fiber (CF) surface modification was developed. The MHTCL is a multiscale high-disorder amorphous carbon coating with a colored appearance, abundant functional groups, multiscale roughness, a large specific surface area, a high surface energy, and good wetting ability. The O/C atom ratios of the MHTCL-modified CF were in the range of 0.17-0.23, and the functional groups were mainly C-O and C?O groups. During the low-concentration glucose hydrothermal treatment with the carbon fibers (CFs), the glucose generates furan derivative intermediates, which adsorb on the surface of the CFs and carbonize continuously, finally forming the MHTCL on the CFs. The fracture and rupture of the MHTCL during the forming process produce new nucleation centers on the CF surface, which result in abundant multiscale irregular particles. The MHTCL is a facile method for the modification of CFs. The fabrication of the CF composites demonstrated that the MHTCL obviously increases the interlaminar shear strength of the CF/polyimide composite and the interfacial interaction of the CF and polyetheretherketone.
关键词Interfacial Shear-strength Sodium-ion Batteries Carbon/carbon Composites Mechanical-properties Surface Modification Carbonization Adhesion Glucose Monosaccharides Reinforcement
学科领域Engineering ; Physics
语种英语
文献类型期刊论文
条目标识符http://ir.nimte.ac.cn/handle/174433/16899
专题2018专题
推荐引用方式
GB/T 7714
Xi, Xianfeng,Chen, Yousi,Wang, Jie,et al. A multiscale hydrothermal carbon layer modified carbon fiber for composite fabrication[J]. RSC ADVANCES,2018,8(41):23339-23347.
APA Xi, Xianfeng.,Chen, Yousi.,Wang, Jie.,Li, Yaoyao.,Shao, Xiangdong.,...&Pei, Xueliang.(2018).A multiscale hydrothermal carbon layer modified carbon fiber for composite fabrication.RSC ADVANCES,8(41),23339-23347.
MLA Xi, Xianfeng,et al."A multiscale hydrothermal carbon layer modified carbon fiber for composite fabrication".RSC ADVANCES 8.41(2018):23339-23347.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Xi, Xianfeng]的文章
[Chen, Yousi]的文章
[Wang, Jie]的文章
百度学术
百度学术中相似的文章
[Xi, Xianfeng]的文章
[Chen, Yousi]的文章
[Wang, Jie]的文章
必应学术
必应学术中相似的文章
[Xi, Xianfeng]的文章
[Chen, Yousi]的文章
[Wang, Jie]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。