Influence of Processing Parameters on Laser Direct Joining of CFRTP and Stainless Steel
Sheng, Liyuan; Jiao, Junke; Du, Beining; Wang, Feiya; Wang, Qiang
2018
Source PublicationADVANCES IN MATERIALS SCIENCE AND ENGINEERING
AbstractThe CFRTP and the stainless steel were joined by the fiber laser, and the effect of processing parameters on the joint quality was investigated in detail.) The heat-affected zone on the stainless steel and the microstructure of the joint interface were examined and analyzed. The results showed that the laser joining process refines the microstructure of the fusion and heat-affected zones in the stainless steel. And the tensile strength of the joint was affected greatly by the laser power and scanning speed but slightly by the clamping pressure. With the PPS additive, the joint shear strength could be improved, and the optimal PPS additive thickness is 300 mu m. With the best parameters, joint with a shear strength of 15-17 MPa could be obtained as the laser power is 320-350 W, the scanning speed is 4-5 mm/s, the clamping pressure is about 0.5 Mpa, and the additive PPS thickness is about 300 mu m.
KeywordFiber-reinforced Polymer Mechanical-properties Polycarbonate Sheets Aluminum Joints Metal Microstructure Failure Alloy
Subject AreaMaterials Science
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/16904
Collection2018专题
Recommended Citation
GB/T 7714
Sheng, Liyuan,Jiao, Junke,Du, Beining,et al. Influence of Processing Parameters on Laser Direct Joining of CFRTP and Stainless Steel[J]. ADVANCES IN MATERIALS SCIENCE AND ENGINEERING,2018.
APA Sheng, Liyuan,Jiao, Junke,Du, Beining,Wang, Feiya,&Wang, Qiang.(2018).Influence of Processing Parameters on Laser Direct Joining of CFRTP and Stainless Steel.ADVANCES IN MATERIALS SCIENCE AND ENGINEERING.
MLA Sheng, Liyuan,et al."Influence of Processing Parameters on Laser Direct Joining of CFRTP and Stainless Steel".ADVANCES IN MATERIALS SCIENCE AND ENGINEERING (2018).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Sheng, Liyuan]'s Articles
[Jiao, Junke]'s Articles
[Du, Beining]'s Articles
Baidu academic
Similar articles in Baidu academic
[Sheng, Liyuan]'s Articles
[Jiao, Junke]'s Articles
[Du, Beining]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Sheng, Liyuan]'s Articles
[Jiao, Junke]'s Articles
[Du, Beining]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.