Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging
Guo, Zhansheng; Fan, Yang; Du, Shiyu
2018
发表期刊JOURNAL OF PLASTIC FILM & SHEETING
卷号34期号:1页码:43399
摘要The heat-seal strength of polymer-metal-polymer laminates, widely used in the packaging industry and more recently for pouch lithium-ion batteries, is a critical factor for the integrity of flexible package structures during service. The influences of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate (LiPF6/EC/DMC) electrolyte soaking time and storage temperature on heat-seal strength were investigated through T-peel testing using a universal testing machine. Sealed multilayer laminates' heat-seal strength and their failure modes were measured for specimens sealed at various heat-sealing temperatures and dwell times before and after exposure to room temperature and 60? soaking conditions. The soaking condition significantly influences heat-seal strength, especially for the packages heat-sealed at low temperatures and short heat-sealing times. Higher storage temperature during electrolyte-soaking accelerates the heat-seal strength decrease. Failure modes are affected by the soaking conditions and become more complicated than the packages without soaking. The optimized heat-sealing processing window is obtained under a certain soaking condition. The electrolyte hydrogen ion concentration (pH) decreases with longer soaking time and higher storage temperature, indicating that acidification may also contribute to decreased heat-seal strength. The results are important for understanding how stored lithium-ion batteries deteriorate and can help to guide battery design to maximize their shelf life.
关键词Low-density Polyethylene Aluminum Foil Corrosion Behavior Adhesion Films Polypropylene Temperature Sorption Layers Acids
学科领域Energy & Fuels
语种英语
文献类型期刊论文
条目标识符http://ir.nimte.ac.cn/handle/174433/16943
专题2018专题
推荐引用方式
GB/T 7714
Guo, Zhansheng,Fan, Yang,Du, Shiyu. Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging[J]. JOURNAL OF PLASTIC FILM & SHEETING,2018,34(1):43399.
APA Guo, Zhansheng,Fan, Yang,&Du, Shiyu.(2018).Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging.JOURNAL OF PLASTIC FILM & SHEETING,34(1),43399.
MLA Guo, Zhansheng,et al."Influence of lithium hexafluorophosphate/ethylene carbonate/dimethyl carbonate electrolyte soaking on heat seal strength of polyamide 6/aluminum/cast-polypropylene laminates used as lithium-ion battery packaging".JOURNAL OF PLASTIC FILM & SHEETING 34.1(2018):43399.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Guo, Zhansheng]的文章
[Fan, Yang]的文章
[Du, Shiyu]的文章
百度学术
百度学术中相似的文章
[Guo, Zhansheng]的文章
[Fan, Yang]的文章
[Du, Shiyu]的文章
必应学术
必应学术中相似的文章
[Guo, Zhansheng]的文章
[Fan, Yang]的文章
[Du, Shiyu]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。