Preparation and formation mechanism of size-controlled lignin based microsphere by reverse phase polymerization
Yu, Baojun; Chang, Zhenzhen; Zhang, Yang; Wang, Chengyang
2018
发表期刊MATERIALS CHEMISTRY AND PHYSICS
卷号203页码:97-105
摘要Commercial lignin, by-product of enzymatic hydrolysis of biomass for bioethanol production, was used to prepare lignin based microsphere by reverse phase polymerization. The reverse phase polymerization had favorable influence on the morphology, size distribution and thermal stability by coordinating solid content and dispersed phase content of lignin emulsion. The carbonization yield at 870 degrees C of lignin based microsphere reaches to 38.87% by improving 5% from lignin precursor 33.43%, at solid content 0.059 and dispersed phase content 0.050. The mechanism is postulated based on the results from elemental analysis, FT-IR spectroscopy and thermogravimetric analysis. Furthermore, the lignin based microsphere could directly carbonize without pre-oxidization process. Hence, the reverse phase polymerization is a meaningful and possible industrial process. And the gravimetric capacitance of lignin based activated carbon microsphere (LAC-M) is as high as 334 F g(-1), and even after 10,000 cycles at 1 A g(-1) a specific capacity of 286 F g(-1) remains. Thus, LAC-M is a promising material for high performance SCs. (C) 2017 Published by Elsevier B.V.
关键词Carbon-fibers Emulsion Polymerization Acid) Composites Resin Conversion Blends
学科领域Materials Science ; Physics
语种英语
文献类型期刊论文
条目标识符http://ir.nimte.ac.cn/handle/174433/16954
专题2018专题
推荐引用方式
GB/T 7714
Yu, Baojun,Chang, Zhenzhen,Zhang, Yang,et al. Preparation and formation mechanism of size-controlled lignin based microsphere by reverse phase polymerization[J]. MATERIALS CHEMISTRY AND PHYSICS,2018,203:97-105.
APA Yu, Baojun,Chang, Zhenzhen,Zhang, Yang,&Wang, Chengyang.(2018).Preparation and formation mechanism of size-controlled lignin based microsphere by reverse phase polymerization.MATERIALS CHEMISTRY AND PHYSICS,203,97-105.
MLA Yu, Baojun,et al."Preparation and formation mechanism of size-controlled lignin based microsphere by reverse phase polymerization".MATERIALS CHEMISTRY AND PHYSICS 203(2018):97-105.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Yu, Baojun]的文章
[Chang, Zhenzhen]的文章
[Zhang, Yang]的文章
百度学术
百度学术中相似的文章
[Yu, Baojun]的文章
[Chang, Zhenzhen]的文章
[Zhang, Yang]的文章
必应学术
必应学术中相似的文章
[Yu, Baojun]的文章
[Chang, Zhenzhen]的文章
[Zhang, Yang]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。