Effects of Si content on Tribo-corrosion behavior of Cr1-xSixN coatings prepared via magnetron sputtering
Shao, Tao; Ge, Fangfang; Pei, Chenrui; Huang, Feng; Sun, Deen; Zhang, Sam
2018
Source PublicationSURFACE & COATINGS TECHNOLOGY
Volume356Pages:43422
AbstractTribo-corrosion behavior of the magnetron sputtering Cr1-xSixN coatings with various Si content was investigated under different testing conditions. The tests were performed using a linear reciprocation ball-on-plate tribometer in the atmosphere, with 3.5 wt% NaCl and under cathodic protection condition. Though Cr0.58Si0.42N exhibited best wear resistance in tribological test and good corrosion resistance in corrosion test, the tribo-corrosion resistance was not significantly improved. Meanwhile, Cr0.96Si0.04N exhibited the lowest wear rate of 1.5 x 10(-15) m(3)/N m during tribo-corrosion test. It has been found that in the process of tribo-corrosion test, in addition to considering both the corrosion resistance and wear resistance of the coating, more attention should be paid to its tribochemical reaction property which caused increased embrittlement under salt water environment.
KeywordStainless-steel Tribological Properties Crn Coatings n Coatings Thin-films Tribocorrosion Pvd Environments System Air
Subject AreaChemistry ; Polymer Science
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/16964
Collection2018专题
Recommended Citation
GB/T 7714
Shao, Tao,Ge, Fangfang,Pei, Chenrui,et al. Effects of Si content on Tribo-corrosion behavior of Cr1-xSixN coatings prepared via magnetron sputtering[J]. SURFACE & COATINGS TECHNOLOGY,2018,356:43422.
APA Shao, Tao,Ge, Fangfang,Pei, Chenrui,Huang, Feng,Sun, Deen,&Zhang, Sam.(2018).Effects of Si content on Tribo-corrosion behavior of Cr1-xSixN coatings prepared via magnetron sputtering.SURFACE & COATINGS TECHNOLOGY,356,43422.
MLA Shao, Tao,et al."Effects of Si content on Tribo-corrosion behavior of Cr1-xSixN coatings prepared via magnetron sputtering".SURFACE & COATINGS TECHNOLOGY 356(2018):43422.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Shao, Tao]'s Articles
[Ge, Fangfang]'s Articles
[Pei, Chenrui]'s Articles
Baidu academic
Similar articles in Baidu academic
[Shao, Tao]'s Articles
[Ge, Fangfang]'s Articles
[Pei, Chenrui]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Shao, Tao]'s Articles
[Ge, Fangfang]'s Articles
[Pei, Chenrui]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.