Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use
Han, Jin; Chen, Cheng; Xue, Qingquan; Zheng, Yaochen; Tian, Shu; Liu, Zhixiong; Shen, Jieze; Zhong, Mingqiang
2018
Source PublicationPOLYMER
Volume154Pages:43107
AbstractA catalyst-free and thermal-induced S -> O acetyl migration (SOAM) reaction was occasionally found and used to fabricate the polythiol corrosion inhibitor. The route to prepare the polythiols was free of catalyst and side products. Only intramolecular migration process existed, while intermolecular migration was not found. Temperature-dependent H-1 NMR experiment showed the conversion rate of the SOAM reaction was 83% at 160 degrees C. Further heating at higher temperature or for longer reaction time, the conversion rate did not increase. It was speculated that there was equilibrium between two reversible migrations. The prepared polythiol inhibitor contains a large amount of latent thiol groups after the SOAM reaction process. The strong Cu-S bonds immediately formed and made the polythiol chains firmly anchored on the copper surface when the copper metal was coated with the polythiols. Also S-S bond formation reaction leads to dense crosslinking and film formation. Raman spectrum and SEM were used to characterized the protective film. A smooth and defect-free film with thickness of 1.9 mu m was achieved when the copper sample was immersed in the polythiol solution for 60 min. The corrosion performance of the film is obtained by potential and impedance measurements and Tafel curves by immersing in a 3.5 wt% NaCl solution. All of the coated samples exhibited significantly lower corrosion rates than the bare copper sample, and the corrosion rate decreased as the immersion time increased. The inhibtion efficiency of the polythiol inhibitor was up to 99.3%. Neutral salt spray experiments indicated that the polythiol films provided excellent protection for over one week. The polythiols were also very stable in storage and have application in designing various polyacrylate polythiols resins.
KeywordSol-gel Coatings Copper Corrosion Surface Modification Click Reaction Protection Chemistry Metals Inhibitors Delivery
Subject AreaPhysics
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/17131
Collection2018专题
Recommended Citation
GB/T 7714
Han, Jin,Chen, Cheng,Xue, Qingquan,et al. Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use[J]. POLYMER,2018,154:43107.
APA Han, Jin.,Chen, Cheng.,Xue, Qingquan.,Zheng, Yaochen.,Tian, Shu.,...&Zhong, Mingqiang.(2018).Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use.POLYMER,154,43107.
MLA Han, Jin,et al."Catalyst-free and thermal-induced S -> O acetyl migration reaction to generate the polyacrylate polythiols for anticorrosion use".POLYMER 154(2018):43107.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Han, Jin]'s Articles
[Chen, Cheng]'s Articles
[Xue, Qingquan]'s Articles
Baidu academic
Similar articles in Baidu academic
[Han, Jin]'s Articles
[Chen, Cheng]'s Articles
[Xue, Qingquan]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Han, Jin]'s Articles
[Chen, Cheng]'s Articles
[Xue, Qingquan]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.