Composition anisotropy compensation and magnetostriction of Co-doped Laves compounds Tb0.2Dy0.8-xPrxFe1.93 (0 <= x <= 0.40)
Li, F.; Liu, J. J.; Zhu, X. Y.; Shen, W. C.; Lin, L. L.; Du, J.; Si, P. Z.
2018
Source PublicationSOLID STATE COMMUNICATIONS
Volume275Pages:63-67
AbstractAlloys of Tb0.2Dy0.8-xPrx(Fe0.8Co0.2)(1.93) (0 <= x <= 0.40) are arc melted and investigated for structural, magnetic and magnetoelastic by means of x-axis diffraction (XRD), a vibrating sample magnetometer and a standard strain technique. The 20 at % Co substitution for Fe is shown to enable the formation of the single Laves phase with a high Pr content up to x = 0.25. Experimental evidence for magnetocrystalline-anisotropy compensation between Pr3- and Dy3- ions is obtained in the Laves phase system. The easy magnetization direction (EMD) at room temperature rotates from <100> to <110> axis when x increases from 0 to 0.40. The linear anisotropic magnetostriction lambda(a)(=lambda(parallel to)-lambda(perpendicular to)) increases with increasing Pr content when x < 0.25 ascribed to both the larger magnetostriction of PrFe2 than that of DyFe2 and the decrease of the resulted anisotropy due to compensation. The composition anisotropy compensation is found to be around x = 0.25, shifting to the Pr-rich side at room temperature as compared to the Co-free counterpart Tb0.2Dy0.8-xPrxFe1.93 system. The Tb0.2Dy0.55Pr0.25(-Fe0.8Co0.2)(1.93) alloy has good magnetoelastic properties at room temperature, that is, a low anisotropy and a high low-field magnetostriction lambda(a)similar to 140 ppm at 1 kOe.
KeywordIntermetallic Compounds Alloys
Subject AreaPolymer Science
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/17364
Collection2018专题
Recommended Citation
GB/T 7714
Li, F.,Liu, J. J.,Zhu, X. Y.,et al. Composition anisotropy compensation and magnetostriction of Co-doped Laves compounds Tb0.2Dy0.8-xPrxFe1.93 (0 <= x <= 0.40)[J]. SOLID STATE COMMUNICATIONS,2018,275:63-67.
APA Li, F..,Liu, J. J..,Zhu, X. Y..,Shen, W. C..,Lin, L. L..,...&Si, P. Z..(2018).Composition anisotropy compensation and magnetostriction of Co-doped Laves compounds Tb0.2Dy0.8-xPrxFe1.93 (0 <= x <= 0.40).SOLID STATE COMMUNICATIONS,275,63-67.
MLA Li, F.,et al."Composition anisotropy compensation and magnetostriction of Co-doped Laves compounds Tb0.2Dy0.8-xPrxFe1.93 (0 <= x <= 0.40)".SOLID STATE COMMUNICATIONS 275(2018):63-67.
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li, F.]'s Articles
[Liu, J. J.]'s Articles
[Zhu, X. Y.]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li, F.]'s Articles
[Liu, J. J.]'s Articles
[Zhu, X. Y.]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li, F.]'s Articles
[Liu, J. J.]'s Articles
[Zhu, X. Y.]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.