Controllable SiO2 coating layer of FeSiBPNb amorphous powder cores with excellent soft magnetic properties
Huang, Ke-yu; Dong, Ya-qiang; Liu, Min; Ren, Ji-hang; Lu, Shu-han; Zhao, Zhan-kui; Chang, Chun-tao; Wang, Xin-min
2018
发表期刊JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL
卷号25期号:6页码:624-629
摘要Amorphous powder cores based on spherical (Fe0.76Si0.09B0.1P0.05)(99)Nb-1 amorphous powder and their SiO2 layer prepared by in situ coating insulation process were investigated in detail. These cores were characterized by scanning electron microscopy and X-ray diffraction analyses, and the results revealed that the surface layer of the amorphous powder was composed of SiO2 with uniform surface coverage. The thickness of the SiO2 insulating layer could be controlled by adjusting the tetraethyl orthosilicate (TEOS) content. By cold-pressing with epoxy resin under a pressure of 1800 MPa, a ring powder core with an outer diameter of 20.3 mm, inner diameter of 12.7 mm, and height of 5.3 mm was prepared. The FeSiBPNb composite core showed its best properties when the TEOS content was 2 mL/g (the volume of TEOS for each gram of (Fe0.76Si0.09B0.1P0.05)(99)Nb-1 amorphous powder, mL/g), which showed good relative permeability in the high-frequency range of up to 10 MHz and a low core loss of 320 W/kg under the maximum magnetic flux density of 0.1 T and frequency of 100 kHz.
关键词Alloy Powder Eddy-current Fe Composites Magnetostriction Fabrication Size
学科领域Engineering ; Materials Science ; Physics
语种英语
文献类型期刊论文
条目标识符http://ir.nimte.ac.cn/handle/174433/17425
专题2018专题
推荐引用方式
GB/T 7714
Huang, Ke-yu,Dong, Ya-qiang,Liu, Min,et al. Controllable SiO2 coating layer of FeSiBPNb amorphous powder cores with excellent soft magnetic properties[J]. JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,2018,25(6):624-629.
APA Huang, Ke-yu.,Dong, Ya-qiang.,Liu, Min.,Ren, Ji-hang.,Lu, Shu-han.,...&Wang, Xin-min.(2018).Controllable SiO2 coating layer of FeSiBPNb amorphous powder cores with excellent soft magnetic properties.JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL,25(6),624-629.
MLA Huang, Ke-yu,et al."Controllable SiO2 coating layer of FeSiBPNb amorphous powder cores with excellent soft magnetic properties".JOURNAL OF IRON AND STEEL RESEARCH INTERNATIONAL 25.6(2018):624-629.
条目包含的文件
条目无相关文件。
个性服务
推荐该条目
保存到收藏夹
查看访问统计
导出为Endnote文件
谷歌学术
谷歌学术中相似的文章
[Huang, Ke-yu]的文章
[Dong, Ya-qiang]的文章
[Liu, Min]的文章
百度学术
百度学术中相似的文章
[Huang, Ke-yu]的文章
[Dong, Ya-qiang]的文章
[Liu, Min]的文章
必应学术
必应学术中相似的文章
[Huang, Ke-yu]的文章
[Dong, Ya-qiang]的文章
[Liu, Min]的文章
相关权益政策
暂无数据
收藏/分享
所有评论 (0)
暂无评论
 

除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。