Thick CrN/AlN superlattice coatings deposited by hot filament assisted HiPIMS for solid particle erosion and high temperature wear resistance
Lin, Jianliang; Zhang, Xuhai; Ge, Fangfang; Huang, Feng
2019
Source PublicationSURFACE & COATINGS TECHNOLOGY
Volume377
AbstractThick CrN/AlN superlattice coatings deposited by hot filament assisted HiPIMS for solid particle erosion and high temperature wear resistance
KeywordOXIDATION BEHAVIOR MAGNETRON MICROSTRUCTURE HARDNESS FILMS CRALN
DOI10.1016/j.surfcoat.2019.124922
Citation statistics
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/17844
Collection2019专题
AffiliationLin, JL (reprint author), Southwest Res Inst, San Antonio, TX 78238 USA.
First Author Affilication中国科学院宁波材料技术与工程研究所
Recommended Citation
GB/T 7714
Lin, Jianliang,Zhang, Xuhai,Ge, Fangfang,et al. Thick CrN/AlN superlattice coatings deposited by hot filament assisted HiPIMS for solid particle erosion and high temperature wear resistance[J]. SURFACE & COATINGS TECHNOLOGY,2019,377.
APA Lin, Jianliang,Zhang, Xuhai,Ge, Fangfang,&Huang, Feng.(2019).Thick CrN/AlN superlattice coatings deposited by hot filament assisted HiPIMS for solid particle erosion and high temperature wear resistance.SURFACE & COATINGS TECHNOLOGY,377.
MLA Lin, Jianliang,et al."Thick CrN/AlN superlattice coatings deposited by hot filament assisted HiPIMS for solid particle erosion and high temperature wear resistance".SURFACE & COATINGS TECHNOLOGY 377(2019).
Files in This Item:
There are no files associated with this item.
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Lin, Jianliang]'s Articles
[Zhang, Xuhai]'s Articles
[Ge, Fangfang]'s Articles
Baidu academic
Similar articles in Baidu academic
[Lin, Jianliang]'s Articles
[Zhang, Xuhai]'s Articles
[Ge, Fangfang]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Lin, Jianliang]'s Articles
[Zhang, Xuhai]'s Articles
[Ge, Fangfang]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.