Thermoelectric properties of hot-pressed Zn4Sb3−xTex
Li W ; Zhou LM ; Li YL ; Jiang J ; Xu GJ
2009
Source PublicationJournal of Alloys and Compounds
Issue486Pages:335–337
AbstractA series of samples have been fabricated through vacuum melting method followed by hot-pressing for Zn4Sb3−xTex (x = 0.02–0.08), XRD patterns indicated that all the samples were single-phased β-Zn4Sb3. Electrical conductivity and Seebeck coefficient were evaluated in the temperature range of 300–700 K, showing p-type conduction. The thermoelectric figure of merit (ZT) was increased with the increase of Te content. ZT values of 0.8 and 1.0 were obtained at 673K for Zn4.08Sb3 and Zn4Sb2.92Te0.08, respectively.; A series of samples have been fabricated through vacuum melting method followed by hot-pressing for Zn4Sb3−xTex (x = 0.02–0.08), XRD patterns indicated that all the samples were single-phased β-Zn4Sb3. Electrical conductivity and Seebeck coefficient were evaluated in the temperature range of 300–700 K, showing p-type conduction. The thermoelectric figure of merit (ZT) was increased with the increase of Te content. ZT values of 0.8 and 1.0 were obtained at 673K for Zn4.08Sb3 and Zn4Sb2.92Te0.08, respectively.
KeywordΒ-zn4sb3 Thermoelectric Properties Hot-pressing Method
Indexed BySCI
Language英语
Document Type期刊论文
Identifierhttp://ir.nimte.ac.cn/handle/174433/206
Collection宁波所知识产出
Recommended Citation
GB/T 7714
Li W,Zhou LM,Li YL,et al. Thermoelectric properties of hot-pressed Zn4Sb3−xTex[J]. Journal of Alloys and Compounds,2009(486):335–337.
APA Li W,Zhou LM,Li YL,Jiang J,&Xu GJ.(2009).Thermoelectric properties of hot-pressed Zn4Sb3−xTex.Journal of Alloys and Compounds(486),335–337.
MLA Li W,et al."Thermoelectric properties of hot-pressed Zn4Sb3−xTex".Journal of Alloys and Compounds .486(2009):335–337.
Files in This Item:
File Name/Size DocType Version Access License
Thermoelectric prope(457KB) 开放获取LicenseApplication Full Text
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Li W]'s Articles
[Zhou LM]'s Articles
[Li YL]'s Articles
Baidu academic
Similar articles in Baidu academic
[Li W]'s Articles
[Zhou LM]'s Articles
[Li YL]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Li W]'s Articles
[Zhou LM]'s Articles
[Li YL]'s Articles
Terms of Use
No data!
Social Bookmark/Share
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.